LNP™ THERMOCOMP™ UF0037W compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gCqD08_LNP-THERMOCOMP-UF0037W-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* UF13HWZ270 is a compound based on Polyphthalamide resin containing Glass Fiber. Added features of this material include: Heat Stabilized, Non-Brominated & Non-Chlorinated Flame Retardant. Also known as: LNP* THERMOCOMP* Compound UF-1003 HW Z270 Product reorder name: UF0037W |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.33 | g/cm³ | ASTM D792 |
| -- | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.50 to 0.90 | % | |
| Across Flow : 24 hr | 1.5 to 1.9 | % | |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8480 | MPa | ASTM D638 |
| -- | 8300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 113 | MPa | ASTM D638 |
| Yield | 106 | MPa | ISO 527-2 |
| Break | 113 | MPa | ASTM D638 |
| Break | 106 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.3 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Break | 2.3 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7580 | MPa | ASTM D790 |
| -- | 6300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 179 | MPa | ASTM D790 |
| -- | 174 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 4.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 340 | J/m | ASTM D4812 |
| 23°C 3 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.20 | J | ASTM D3763 |
| -- | 1.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 271 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 270 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.2E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® HT NT40 GR60 NL HS | Eurotec Engineering Plastics | PPA | Tecomid® HT |
| Cogegum® GFR/340 | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |
| LNP™ LUBRILOY™ RF208 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| Lusin® Protect G 31 | Chem-Trend L.P. | Unspecified | Lusin® |
| Aquivion® PW79S-Li | Solvay Specialty Polymers | PFSA Lithium Salt | Aquivion® |