Ebalta GH 706 / GLE
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gCbsgs_Ebalta-GH-706-GLE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta GH 706/GLE is a well castable two-components epoxy resin, which cures at room temperature and can be casted till 20 mm thickness. The resin GH 706 contains very fine hard fillers and with hardener GLE it has got a very hard, wear resistant surface with high compression strength and impact resistance. ebalta GH 706 is the castable version of the very hard gelcoat OH 6-1. Applications
Properties
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | 0.11 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 87 to 93 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 6150 to 7350 | MPa | ISO 178 |
| Flexural Stress | 77.0 to 93.0 | MPa | ISO 178 |
| Compressive Stress | 78.0 to 94.0 | MPa | ISO 604 |
| Taber Abrasion Resistance (250 Cycles, 1000 g, CS-10 Wheel) | 23.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 7.0 to 11 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 48.0 to 52.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 18 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 2.00 to 2.10 | g/cm³ | |
| Viscosity (25°C) | 8.0 to 12 | Pa·s | |
| Curing Time (20°C) | 12 to 16 | hr | |
| Pot Life 1(20°C) | 30 to 40 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ROPOTEN® K-12-110-065 | LUKOIL Bulgaria Ltd. | LDPE | ROPOTEN® |
| Vinylbond 6527P-MD Grey 499 | Colorite Polymers | PVC, Flexible | Vinylbond |
| Nymax™ GMF 604 40 UV Black 115 1 X 1 | PolyOne Corporation | Nylon 6 | Nymax™ |
| DuraFlex 767 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraFlex |
| Hyundai EP PA66 LD950 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |