MARPOL® LL8F 805
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gCZ9yS_MARPOLLL8F805.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Features: Good stiffness, easy processability, moderate toughness, moderate strength and excellent seal properties Recommended Applications: Heavy duty shipping sacks, industrial packaging, industrial liners, construction film and automatic packaging film |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.927 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 234 | MPa | ASTM D882 |
| 1% sectioning, MD : 76 µm | 230 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 251 | MPa | ASTM D882 |
| 1% sectioning, TD : 76 µm | 260 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 11.0 | MPa | ASTM D882 |
| MD : Yield, 76 µm | 12.4 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 12.4 | MPa | ASTM D882 |
| TD : Yield, 76 µm | 12.4 | MPa | ASTM D882 |
| MD : Break, 25 µm | 42.7 | MPa | ASTM D882 |
| MD : fracture, 76 µm | 41.4 | MPa | ASTM D882 |
| TD : Break, 25 µm | 33.1 | MPa | ASTM D882 |
| TD : fracture, 76 µm | 35.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 490 | % | ASTM D882 |
| MD : fracture, 76 µm | 630 | % | ASTM D882 |
| TD : Break, 25 µm | 710 | % | ASTM D882 |
| TD : fracture, 76 µm | 680 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709A | ||
| 25 µm | 160 | g | ASTM D1709A |
| 76 µm | 450 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 300 | g | ASTM D1922 |
| MD : 76 µm | 1100 | g | ASTM D1922 |
| TD : 25 µm | 750 | g | ASTM D1922 |
| TD : 76 µm | 1500 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 220 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 25.4 µm | 50 | ASTM D2457 | |
| 45°, 76.2 µm | 61 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 25.4 µm | 14 | % | ASTM D1003 |
| 76.2 µm | 17 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA610 A6G7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 610 | Shandong PA610 |
| TOLEN H274 FF | SIBUR, LLC | PP Homopolymer | TOLEN |
| DENITER C | Vamp Tech | PC+PBT | DENITER |
| Dutral® CO 054 | Versalis S.p.A. | EPDM | Dutral® |
| LUVOCOM® TPI-0953 | Lehmann & Voss & Co. | PI, TP | LUVOCOM® |