| U Series Resin Composite Grade |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 0.25 | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.13 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 73.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.5 | % | ASTM D638 |
| Flexural Modulus | 4700 | MPa | ASTM D790 |
| Flexural Strength | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 98.0 | °C | ASTM D648 |
| CLTE - Flow | 2.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITIKA Nylon 6 A1030FR | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| DOMAMID® 66STZ | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Durethan® BKV 30 H3.0 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Loyblend® HA-1700 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS+Acrylic | Loyblend® |
| PLUSTEK RA843 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |