PPR PA602
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Premier Plastic Resins, Inc. |
| Trademark: | PPR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gCD0pf_PPR-PA602.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 6 13% Glass Fiber Reinforced Heat Stabilized Natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 107 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 5170 | MPa | ASTM D790 |
| Flexural Strength | 168 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 213 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 193 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.0 - 82.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 238 - 282 | °C | |
| Middle Temperature | 249 - 293 | °C | |
| Front Temperature | 249 - 293 | °C | |
| Nozzle Temperature | 243 - 288 | °C | |
| Processing (Melt) Temp | 254 - 299 | °C | |
| Mold Temperature | 66.0 - 93.0 | °C | |
| Injection Pressure | 14.0 - 103 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 10.0 - 83.0 | MPa | |
| Back Pressure | 0.00 - 1.00 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Screw Speed: Slow-ModerateDecompression: 3.81 to 7.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® SI 9002 | Vyncolit N.V. | Silicone | Vyncolit® |
| Ultramid® A3EG5 | BASF Corporation | Nylon 66 | Ultramid® |
| EMERGE™ PC 8210-15 | Trinseo | PC | EMERGE™ |
| LNP™ STAT-KON™ MD000AP compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |
| PETILEN I10-19T | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |