TAROLOX 10 G5
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gBgr0n_TAROLOX-10-G5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROLOX 10 G5 is a Polybutylene Terephthalate (PBT) product filled with 25% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 to 1.50 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.60 to 1.0 | % | |
| Flow | 0.40 to 0.60 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.045 | % | |
| Saturation, 23°C | 0.24 | % | |
| Granule Humidity 1 | < 0.050 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 115 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 7500 | MPa | ISO 178 |
| Flexural Stress 3 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 65 | J/m | |
| 23°C | 76 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed | 218 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 208 | °C | ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 5 | 90.0 | °C | |
| -- 6 | 130 | °C | |
| Vicat Softening Temperature | |||
| -- | 216 | °C | ISO 306/A50 |
| -- | 212 | °C | ISO 306/B50 |
| Ball Pressure Test (215°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 220 to 225 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.60 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 450 | V | |
| Solution B | 200 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 20 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| 5 . | 20000 hrs |
| 6 . | Short Term |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE 9658 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| XANTAR® MX 2042 FD | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| CompaDur® 125 GF 30 black (047) | DimeLika Plast GmbH | PBT+PET | CompaDur® |
| GAPEX® RPP20EU78BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Crastin® T843FR NC010 | DuPont Performance Polymers | PBT | Crastin® |