Elastollan® B 95 A 11 FC
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gALmsg_ElastollanB95A11FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermoplastic Polyester-Polyurethane with excellent mechanical properties, outstanding wear resistance, high tear and tensile strength, good damping characteristic, high resilience performance and superior low temperature flexibility. General suitability for food contact related applications in FDA and EU regulated markets (please see food contact information) |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3 sec) | 53 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 30.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 7.00 | MPa | DIN 53504-S2 |
| 100% strain | 10.0 | MPa | DIN 53504-S2 |
| 300% strain | 22.0 | MPa | DIN 53504-S2 |
| Tensile Stress (Yield) | 55.0 | MPa | DIN 53504-S2 |
| Tensile Elongation (Break) | 550 | % | DIN 53504-S2 |
| Tear Strength 1 | 100 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 30 | % | ISO 815 |
| 70°C, 24 hr | 40 | % | ISO 815 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 | °C | |
| Rear Temperature | 210 - 220 | °C | |
| Middle Temperature | 215 - 225 | °C | |
| Front Temperature | 220 - 230 | °C | |
| Nozzle Temperature | 220 - 230 | °C | |
| Processing (Melt) Temp | 220 - 230 | °C | |
| Mold Temperature | 20 - 40 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 - 15.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 175 - 195 | °C | |
| Cylinder Zone 2 Temp. | 185 - 205 | °C | |
| Cylinder Zone 3 Temp. | 195 - 215 | °C | |
| Cylinder Zone 4 Temp. | 205 - 220 | °C | |
| Adapter Temperature | 210 - 230 | °C | |
| Die Temperature | 195 - 215 | °C |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROBLEND 50 X0 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| VESTODUR® GF10 | Evonik Industries AG | PBT | VESTODUR® |
| Topilene® J945 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Karina NATURAL PVC COMPOUND -E 730D25/ 1-IS-WK | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9600-60 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |