Glass-fibre reinforced Polyester moulding compound

Low mould shrinkage and post-shrinkage, good electrical values, good heat resistance, good mechanical strength

Primary application(s): moulded parts in electrical engineering

This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS)

Identification according to ISO 14530-3: UP (GF10 + MD65) - (GF20 + MD55)
DIN 7708: UP 804

General Information
Filler / Reinforcement	Glass Fiber
Features	Good Electrical Properties Good Strength Low Shrinkage Medium Heat Resistance
Uses	Electrical Parts
Agency Ratings	EU 2002/96/EC (WEEE) EU 2006/122/EC
RoHS Compliance	RoHS Compliant
Forms	Granules
Processing Method	Compression Molding Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.90 to 2.10	g/cm³	ISO 1183
Apparent Density	0.75 to 1.00	g/cm³	ISO 60
Molding Shrinkage - Flow			ISO 2577
-- ¹	0.40 to 0.70	%
-- ²	0.20 to 0.50	%
Water Absorption (23°C, 24 hr)	< 0.50	%	ISO 62
Post Shrinkage ³	< 0.10	%	ISO 2577

Thermal	Nominal Value	Unit	Test Method
Maximum Service Temperature			IEC 60216
<50 h	210	°C
20,000 h	180	°C

Additional Information	Nominal Value	Unit
Compression Molding Molding Pressure	> 10.0	MPa
Compression Molding Temperature	165 to 180	°C

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus			ISO 527-2
Compression Molded	6000 to 9000	MPa
Injection Molded	6000 to 9000	MPa
Tensile Stress			ISO 527-2
Compression Molded	35.0 to 60.0	MPa
Injection Molded	40.0 to 70.0	MPa
Flexural Modulus			ISO 178
Compression Molded	8000 to 12000	MPa
Injection Molded	8000 to 12000	MPa
Flexural Stress			ISO 178
Compression Molded	80.0 to 100	MPa
Injection Molded	100 to 120	MPa
Compressive Stress	150 to 200	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
Compression Molded	2.5 to 3.5	kJ/m²
Injection Molded	3.0 to 4.0	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
Compression Molded	5.0 to 10	kJ/m²
Injection Molded	8.0 to 11	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, Unannealed	> 175	°C	ISO 75-2/A
8.0 MPa, Unannealed	125 to 150	°C	ISO 75-2/C
CLTE - Flow (50 to 100°C)	1.0E-5 to 2.0E-5	cm/cm/°C	ISO 11359-2
Thermal Conductivity	0.90 to 1.1	W/m/K	ASTM E1461

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+12 to 1.0E+13	ohms	IEC 60093
Volume Resistivity	1.0E+13 to 1.0E+14	ohms·cm	IEC 60093
Electric Strength	25 to 35	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	6.00 5.00
1 MHz	5.00 4.00
Dissipation Factor			IEC 60250
100 Hz	0.010 to 0.030
1 MHz	0.010 to 0.030
Arc Resistance	PLC 4		ASTM D495
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (3.00 mm)	V-0		UL 94
Glow Wire Flammability Index	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature	930	°C	IEC 60695-2-13

Injection	Nominal Value	Unit
Middle Temperature	50.0 to 70.0	°C
Front Temperature	80.0 to 100	°C
Processing (Melt) Temp	100 to 115	°C
Mold Temperature	165 to 180	°C
Back Pressure	1.00 to 1.50	MPa
Screw Speed	70 to 100	rpm

Note Message
1 .	Compression Molded
2 .	Injection Molded
3 .	168 h / 110°C

Resin Grade	Manufacturer	Category	Trademark
Chemlon® 109-14 G	Teknor Apex Company (Chem Polymer)	Nylon 66	Chemlon®
Gallonprene® GP420-9007	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
LUVOCOM® 1105-7786 VP	Lehmann & Voss & Co.	PEEK	LUVOCOM®
MAJORIS AG157 - 7888	AD majoris	PP Homopolymer	MAJORIS
Perflex TPE GP-65TE	CP Chemie Resources (M) Sdn. Bhd.	SEBS	Perflex