Di-Pak™ R-4307FR
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g8uKM2_Di-Pak-R-4307FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RIGID DI-PAK R-4307 A high performance, long working life potting compound for potting/encapsulating units requiring high physical strength and excellent electricals. DI-PAK R-4307 is a holds its mechanical and electrical properties while under the most severe conditions. This is due to its low water absorption, thermal shock resistance, and retention of strength at elevated temperatures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.10 to 0.35 | % | ASTM D2566 |
| Weight - per cubic inch | 27 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 170 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 1.0 | day | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | 99.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 3860 | MPa | ASTM D790 |
| Flexural Strength | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 25 | J/m | ASTM D256 |
| Unnotched Izod Impact | 38 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.39 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.3E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.90 | ||
| 100 kHz | 3.70 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.021 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity (25°C) | 18000 | cP | ASTM D4878 |
| Demold Time (121°C) | 120 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxiglas® MG555 | Maxiglas Corporation | Acrylic (PMMA) | Maxiglas® |
| RTP 200C TFE 20 | RTP Company | Nylon 11 | RTP |
| Nipol® NBR DN306 | Zeon Corporation | NBR | Nipol® NBR |
| Delta ATR-2G40 | Delta Polymers | Acetal (POM) Copolymer | Delta |
| Hybrid B2026I | Ravago Manufacturing Americas, LLC | PC+PBT | Hybrid |