Order Products : sales@su-jiao.com
3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4105
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g8cXpA_3M-Dyneon-TFM-Modified-PTFE-Compound-TFM-4105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 3M™ Dyneon™ TFM™ Modified PTFE Compound 4105 is a Polytetrafluoroethylene (PTFE) product filled with 25% glass fiber. It can be processed by compression molding or sintering and is available in Europe or North America. Typical application: Engineering/Industrial Parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.24 | g/cm³ | ISO 12086 |
| Apparent Density | 0.82 | g/cm³ | ISO 12086 |
| Average Particle Size | 580 | µm | ISO 12086 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 70.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | 370 to 375 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation Under Load 1(23°C, 15 MPa) | 3.50 | % | ASTM D621 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - TD 2(1000 µm) | 14.0 | MPa | ISO 12086 |
| Tensile Elongation - TD 3(Break, 1000 µm) | 420 | % | ISO 12086 |
| Note Message | |
|---|---|
| 1 . | 100 h load, 25 h relaxation |
| 2 . | Measured on sintered moldings |
| 3 . | Measured on sintered moldings |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BMC 610 Special | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Celstran® PA66-GF60-02 P11/14 | Celanese Corporation | Nylon 66 | Celstran® |
| CONTINUUM™ DGDA-2492 NT | The Dow Chemical Company | HDPE | CONTINUUM™ |
| LNP™ THERMOCOMP™ DF006 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |
| LNP™ STAT-LOY™ AF3009 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |