ACCUTECH™ HP0336T30L1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g6keNz_ACCUTECH-HP0336T30L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0336T30L1 is a polypropylene homopolymer (PP Homopoly) product, which contains 30% talc filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 35.0 | MPa | ASTM D638 |
| Fracture | 30.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 12 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 130 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 72.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-7021U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| STYRON A-TECH™ 1115 | Americas Styrenics LLC | PS (HIPS) | STYRON A-TECH™ |
| BioCeres® BC-LBE03 | FuturaMat | Biodeg Polymers | BioCeres® |
| HOPELEN H1500 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| LNP™ STAT-KON™ Ultem_UC1200 compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |