RIALGLASS C 07 JW 15 G
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALGLASS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g6TLYQ_RIALGLASS-C-07-JW-15-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene elastomerized heterphasic copolymer 15% glass fiber reinforced; stabilized for use in contact with lyes and with hot metals; good stiffness and thermal properties; wide impact strength interval. Flowability specific for injection molding; available in versions natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.3 | % | |
| Flow | 0.65 | % | |
| Ash Content | 15 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 4.2 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 45.0 | MPa | |
| Break, 23°C | 43.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 2.7 | % | |
| Break, 23°C | 4.0 | % | |
| Flexural Modulus 1(23°C) | 3000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 27 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 118 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Phenolic FM 4004 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| Network Polymers PP PPB 25 1316 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Electrafil® J-3/CF/40 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| HIPOL™ J858Y | Mitsui Chemicals, Inc. | PP Random Copolymer | HIPOL™ |
| MACOMASS PP MM-PP GF 20 | MACOMASS Verkaufs AG | PP, Unspecified | MACOMASS PP |