STYRON™ 486M
| Category: | PS (HIPS) , High Impact Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g68ATE_STYRON-486M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON™ 486M is a high-impact polystyrene resin with an excellent balance of toughness, stiffness, flow and heat resistance. It is suitable for both injection molding and extrusion applications. Main Characteristics:
Complied with:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| Compression Molded | 1860 | MPa | |
| Injection Molded | 2100 | MPa | |
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 21.4 | MPa | |
| Yield, Injection Molded | 26.9 | MPa | |
| Ultimate, Compression Molded | 17.2 | MPa | |
| Ultimate, Injection Molded | 25.5 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, Compression Molded | 35 | % | |
| Break, Injection Molded | 40 | % | |
| Flexural Modulus | ASTM D790 | ||
| Compression Molded | 1950 | MPa | |
| Injection Molded | 2160 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Compression Molded | 38.6 | MPa | |
| Injection Molded | 50.3 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| Compression Molded | 86 | J/m | |
| Injection Molded | 110 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 73.9 | °C | |
| 1.8 MPa, Annealed | 97.2 | °C | |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1(1.47 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA I LDPE B22/0.25 | ROMPETROL PETROCHEMICALS S.R.L. | LDPE | MIDILENA I |
| Shin-Etsu Elastomer KE-561U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Unichem 8512B-G015 | Colorite Polymers | PVC, Unspecified | Unichem |