Taitalac® 3000H
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g5o5lw_Taitalac-3000H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taitalac®3000H is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America or Asia Pacific region. The processing method is: pipeline extrusion molding or extrusion. Taitalac®The main features of 3000H are:
Taitalac®The typical application areas of 3000H are: water pipes/pipes/drinking water |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 0.50 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | < 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 3.18mm | 39.3 | MPa | ASTM D638 |
| Fracture, 23°C, 3.18mm | 33.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.18 mm) | 60 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | 2070 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 23°C) | 60.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 490 | J/m | ASTM D256 |
| 23°C, 12.7 mm | 330 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 87.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Water Absorption, ASTM D570: <0.3% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 205 - 235 | °C | |
| Middle Temperature | 215 - 245 | °C | |
| Front Temperature | 205 - 235 | °C | |
| Nozzle Temperature | 225 - 245 | °C | |
| Processing (Melt) Temp | 190 - 200 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.483 | MPa | |
| Screw Speed | 30 - 100 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Moderately High to High |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2201 HF | RTP Company | PEEK | RTP |
| VALOX™ 357X resin | SABIC Innovative Plastics Europe | PC+PBT | VALOX™ |
| Fainplast PVC MPH 75 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| EMOPLEN® A 440 T35 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| Sylvin 802-85 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |