MAJORIS BG204 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g5lwzG_MAJORIS-BG204---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BG204 - 8229 is a 20% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in natural, but other colours can be provided on request. BG204 - 8229 has been developed especially for demanding applications in automotive industry. BG204 - 8229 has high rigidity and impact strength, very good long term heat resistancy, good dimensional stability and good creep resistancy also at high temperatures. APPLICATIONS Product requiring very high overall mechanical performance such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 101 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4450 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 75.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | 4600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 41 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 163 | °C | ISO 306/A |
| -- | 128 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Fogging | DIN 75201 | ||
| 100°C/16h | 1.0 | mg | DIN 75201 |
| 100°C/3h | 98 | % | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | 15.0 | µgC/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 283 A | RTP Company | Nylon 6 | RTP |
| ABSCOM® F335 | Polymer Compounders Limited | ABS | ABSCOM® |
| Ferro PP NPP00GW31WH | Ferro Corporation | PP, Unspecified | Ferro PP |
| Hostaform® S 9244 XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Moplen HP522H | LyondellBasell Industries | PP Homopolymer | Moplen |