EOS PA 2201
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | EOS GmbH |
| Trademark: | EOS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g5N5d8_EOS-PA-2201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
PA 2201, a whitish, a bit more translucent polyamide 12 powder, is in compliance with FDA, 21 CFR, §177.1500 9(b) except for alcoholic foodstuff. Apart from that PA 2201 and PA 2200 have identical material properties. Laser-sintered parts made from PA 2201 possess excellent material properties:
Typical applications of the material are fully functional plastic parts of highest quality. Due to the excellent mechanical properties the material is often used to substitute typical injection moulding plastics. The biocompatibility allows its use e.g. for prostheses, the high abrasion resistance allows e.g. the realisation of movable part connections. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 | |
| Ball Indentation Hardness | 78.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1700 | MPa | ISO 527-2 |
| Tensile Stress 2 | 48.0 | MPa | ISO 527-2 |
| Tensile Strain 3(Break) | 15 | % | ISO 527-2 |
| Flexural Modulus 4(23°C) | 1500 | MPa | ISO 178 |
| Flexural Stress 5 | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 4.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 7(23°C) | 53 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 4.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 33 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 181 | °C | ISO 306/A50 |
| -- | 163 | °C | ISO 306/B50 |
| Melting Temperature 8 | 176 | °C | ISO 11357 |
| Note Message | |
|---|---|
| 1 . | X Direction |
| 2 . | Y Direction |
| 3 . | X Direction |
| 4 . | X Direction |
| 5 . | X Direction |
| 6 . | X Direction |
| 7 . | X Direction |
| 8 . | 20°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Homopolymer PP100 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| WPP PP PPC3MF3-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| NuSil MED-4940 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| CALP WW175 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| LNP™ LUBRICOMP™ OCP36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |