AGILITY™ 2001
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AGILITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g50bXM_AGILITY-2001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AGILITY™ 2001 Performance LDPE Resin is a high pressure LDPE resin offering clarity combined with high shrink tension and strength. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.924 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 5.46 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 51 µm | 94.5 | J/cm³ | ASTM D882 |
| TD : 51 µm | 94.9 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm | 250 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 272 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 15.4 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 14.2 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 30.2 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 25.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 440 | % | ASTM D882 |
| TD : Fracture, 51 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 51 µm | 280 | g | ASTM D1922 |
| TD : 51 µm | 570 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 113 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 91 | ASTM D2457 | |
| Haze (50.8 µm) | 4.8 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 231 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 2.5 in. (63.5 mm); 30:1 ratio L/D Screw Type: DSB II Die Gap: 40 mil (1.78mm) Melt Temperature: 448°F (231°C) Output: 10 lb/hr/in. of die circumference Die Diameter: 6 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 50 rpm Frost Line Height: 25 in. (635 mm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J-2041GA | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| Styropor® BFL 495 | BASF Corporation | PS (EPS) | Styropor® |
| CALP WW567 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Globalprene® 9550U | Lee Chang Yung Chemical Industry Corp. | SEBS | Globalprene® |
| Hifax EKC 244X Black | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |