AKROMID® C3 1 black (4546)
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g4xIGG_AKROMID-C3-1-black-4546-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® C3 1 black (4546) is a nonreinforced, heat stabilised polyamide 6.6/6-Blend. Applications are housings and fixtures in the automotive and electric industry. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 160 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.9 | -- | % | |
| Flow | 1.2 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.6 | -- | % | ISO 1110 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 90 to 120 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 100 to 140 | -- | °C |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 80.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 5.0 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3000 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 115 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 185 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 260 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Evolue™ SP0510 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| Grilon® XE 5052 (BGZ-15 FC) | EMS-GRIVORY | Nylon 6 | Grilon® |
| HiFill® PPA GF35 HS LAHW BK MB | Techmer Engineered Solutions | PPA | HiFill® |
| Sylvin 6185-80 Orange 562 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| KMI KM 757ABS | KMI Group, Inc. | ABS | KMI |