China PPS hGR60
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g4vZts_China-PPS-hGR60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS-hGR60 is glass reinforced PPS compound, which is filled with glass fiber based on the PPS resin. The characteristic of PPS compounds includes good mechanical properties, high rigidity, high creep resistance, high temperature resistance, flame resistance, chemical resistance, excellent electrical insulation properties, arc resistance, low water absorption, low mold shrinkage, easy processing, good dimensional stability, and radiation resistance. Owing to its high performance, PPS-hGR60 is widely used in space aviation, chemical, electronic appliances, mechanical, automobile, railway fields etc. It can be used to make elements where high temperature resistance, electrical insulation are all-important in aviation; anticorrosion valves and electrical insulating parts; precise plugs; parts of engines, terminal etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.78 | g/cm³ | Internal method |
| Molding Shrinkage | Internal method | ||
| Flow | 0.25 | % | Internal method |
| Transverse flow | 0.75 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness 1 | 112 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 162 | MPa | Internal method |
| Tensile Elongation (Break) | 1.7 | % | Internal method |
| Flexural Modulus | 19400 | MPa | Internal method |
| Flexural Strength | 250 | MPa | Internal method |
| Compressive Strength | 137 | MPa | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 12 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 267 | °C | Internal method |
| Melting Temperature | 282 | °C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.5E+15 | ohms | Internal method |
| Volume Resistivity | 2.1E+16 | ohms·cm | Internal method |
| Dielectric Strength | 17 | kV/mm | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 - 180 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 6 to 24hr |
| Note Message | |
|---|---|
| 1 . | HRL |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TATREN® IM 25 75 | Slovnaft Petrochemicals, s.r.o. | PP Impact Copolymer | TATREN® |
| Cri-Line LC-612-THK | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| PLUSTEK RB506 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Sylvin 2946-75 White 1547 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VALOX™ DR51 resin | SABIC Innovative Plastics | PBT | VALOX™ |