Reny® NXG5945S
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g4muVL_Reny-NXG5945S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® NXG5945S is a Polyarylamide (PARA) material filled with 45% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® NXG5945S: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.52 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 13 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 8.50 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.32 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.73 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16000 | 15400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 208 | 202 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 2.2 | % | ISO 527-2 |
| Flexural Modulus | 14300 | 14000 | MPa | ISO 178 |
| Flexural Stress | 349 | 315 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 90 | 77 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 232 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature | 87.0 | -- | °C | ISO 11357-2 |
| Melting Temperature | 257 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.1E-5 | -- | cm/cm/°C | |
| Transverse | 5.6E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.20 | 4.60 | ||
| 1 MHz | 4.10 | 4.20 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.5E-3 | 0.020 | ||
| 1 MHz | 6.7E-3 | 0.012 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 280 | °C | |
| Middle Temperature | 285 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-FR-IM | Polymer Resources Ltd. | PBT | PRL |
| Delta N66R-1G70 | Delta Polymers | Nylon 66 | Delta |
| Gallonprene® GP410-8202 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| GETILAN GPE/150 | Crosspolimeri S.p.A. | XLPE | GETILAN |
| Karina RED PVC COMPOUND -E 780-42/179-A-IS (C800) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |