Novalloy-B B1500, B1500F
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g4KWzP_Novalloy-B-B1500-B1500F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-B B1500, B1500F is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) material. It is available in Asia Pacific. Primary attribute of Novalloy-B B1500, B1500F: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.70 to 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 42.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 100 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 31 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 101 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 0 | UL 746 | |
| Comparative Tracking Index (3.00 mm) | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) (1.50 mm) | 150 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | 17.0 | mm/min | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | 13 | sec | UL 746 |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 50 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ ABS 5010 | TER HELL PLASTIC GMBH | ABS | TEREZ ABS |
| Next Nylon 66 Prime Series PMG38-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| AIE PPO 9010F-S120D | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| Daelim Po1y® LL-25 | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| Marlex® TRB-432 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |