LUVOCOM® 19-8121 VP Datasheet,Nylon 46,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®19-8121 VP is a polyamide 46 (nylon 46) material, which contains glass and carbon fiber reinforced materials. This product is available in Europe,. LUVOCOM®The main features of 19-8121 VP are: Conductivity Electrostatic protection Good dimensional stability Good stiffness Lubrication Typical application areas include: textile/fiber engineering/industrial accessories Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Glass, carbon fiber reinforced materials
Additive	Lubricant
Features	Good dimensional stability Conductivity Rigid, good Electrostatic discharge protection Good strength Lubrication
Uses	Textile applications Engineering accessories Application in Automobile Field Business equipment
Appearance	Grey

Physical	Nominal Value	Unit	Test Method
Density	1.66	g/cm³	ISO 1183
Molding Shrinkage	0.30 - 0.60	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.0	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	14000	MPa	ISO 527-2
Tensile Stress (Break)	105	MPa	ISO 527-2
Tensile Strain (Yield)	0.90	%	ISO 527-2
Flexural Modulus	12000	MPa	ISO 178
Flexural Stress	150	MPa	ISO 178
Flexural Strain at Flexural Strength	1.2	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	180	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	16	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	150	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+9	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
A	80.0	°C
Vacuum dryer, B	80.0	°C
Drying Time
A	2.0 - 8.0	hr
Vacuum dryer, B	2.0 - 12	hr
Suggested Max Moisture	0.10	%
Rear Temperature	285 - 315	°C
Middle Temperature	305 - 315	°C
Front Temperature	305 - 315	°C
Nozzle Temperature	280 - 330	°C
Processing (Melt) Temp	310	°C
Mold Temperature	120 - 140	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 46 , Polyamide 46
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	g4HoWv_LUVOCOM-19-8121-VP.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
ResMart Ultra PC HF	ResMart	PC	ResMart Ultra
SEMICOSIL® 936 UV	Wacker Chemie AG	Silicone	SEMICOSIL®
SuperLite® SL551600-100 (7.0mm)	Azdel, Inc.	PP, Unspecified	SuperLite®
Hylon® N1033THL	Ravago Manufacturing Americas, LLC	Nylon 66	Hylon®
Hypro-G™ PP-RP2C	Entec Polymers	PP Random Copolymer	Hypro-G™