LNP™ FARADEX™ AS002 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g47HNK_LNP-FARADEX-AS002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* FARADEX* AS002 is a compound based on ABS resin containing 10% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. Also known as: LNP* FARADEX* Compound AS-1002 Product reorder name: AS002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.12 | g/cm³ | ASTM D792 |
| -- | 1.11 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.18 | % | |
| Across Flow : 24 hr | 0.27 | % | |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3000 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 42.7 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2 |
| Break | 39.3 | MPa | ASTM D638 |
| Break | 37.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.2 | % | ASTM D638, ISO 527-2 |
| Break | 8.6 | % | ASTM D638 |
| Break | 3.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2820 | MPa | ASTM D790 |
| -- | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 7.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 290 | J/m | ASTM D4812 |
| 23°C 3 | 20 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 11.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 97.2 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 91.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 87.8 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 78.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+6 | ohms·cm | ASTM D257 |
| Shielding Effectiveness (3.00 mm) | 40 to 55 | dB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 210 to 221 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 254 to 266 | °C | |
| Processing (Melt) Temp | 238 to 254 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren DJ200 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Sylvin 2811-80 White 1437 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| NaturePlast NP EL 006 | NaturePlast | TPE | NaturePlast |
| Jiangsu Sinarise EX8535X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| LG ABS AF364 | LG Chem Ltd. | ABS | LG ABS |