KRATON® D1153 A
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | Kraton Polymers LLC |
| Trademark: | KRATON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g3EAle_KRATON-D1153-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Kraton D1153 A is a clear, linear block copolymer based on styrene and butadiene with bound styrene of 29.5% mass. It is supplied from Europe in the physical form(s) identified below in the grade nomenclature:
Kraton D1153 A is used as a modifier of bitumen or thermoplastics and in compound formulations. It may also find use as an ingredient in formulating adhesives, sealants and coatings. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ISO 2781 |
| Apparent Density | 0.40 | g/cm³ | ASTM D1895B |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ISO 1133 |
| Antioxidant Additive | > 0.10 | % | Internal Method |
| Ash Content | ISO 247 | ||
| AS | 0.10 to 0.40 | % | |
| AT | 0.10 to 0.40 | % | |
| Polystyrene Content | 29 to 31 | % | Internal Method |
| Solution Viscosity - (Toluene) 25%wt (25°C) | 1.4 to 1.9 | Pa·s | Internal Method |
| Total Extractables | < 1.0 | % | Internal Method |
| Volatile Matter | < 0.30 | % | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Molecular Mass of Triblock | 123000 | g/mol | Internal Method |
| Triblock Content | 95 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec, Compression Molded) | 70 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(300% Strain) | 2.90 | MPa | ISO 37 |
| Tensile Strength 2(Yield) | 28.0 | MPa | ISO 37 |
| Tensile Elongation 3(Break) | 800 | % | ISO 37 |
| Note Message | |
|---|---|
| 1 . | Typical properties determined on film cast from toluene solution |
| 2 . | Typical properties determined on film cast from toluene solution |
| 3 . | Typical properties determined on film cast from toluene solution |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2990-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| UBESTA 3030JI9L | UBE Industries, Ltd. | Nylon 12 | UBESTA |
| Chiao Fu PA66 MD212LA10 | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Evoprene™ G 925 | AlphaGary | SEBS | Evoprene™ G |
| Fainplast PVC PH 60/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |