TOTAL Polypropylene PPH 4069
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g2Tzge_TOTAL-Polypropylene-PPH-4069.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPH 4069 is homopolymer with a Melt Flow Index of 4 g/10 min. Polypropylene PPH 4069 is intended for extrusion of high tenacity staple fibres for nonwoven applications. It exhibits excellent spinning properties. Polypropylene PPH 4069 has an anti gas-fading formulation to reduce yellowing in fibres. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1550 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Flexural Modulus | 1450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 85.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 164 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 D SI 2 | RTP Company | Nylon 612 | RTP |
| Wah Hong UP WH-8200-BLK F | Wah Hong Industrial Corp. | Polyester Alloy | Wah Hong UP |
| WINTEC™ WFX6 | Japan Polychem Corporation | PP Random Copolymer | WINTEC™ |
| LNP™ THERMOCOMP™ AX06437 compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
| LUVOCOM® 1-0889-4 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |