ColorRx® ACR-1300MIRXG
| Category: | Acrylic, Unspecified , Acrylic |
| Manufacturer: | LTL Color Compounders, Inc. |
| Trademark: | ColorRx® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g2SGmP_ColorRx-ACR-1300MIRXG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A biocompatible, high flow, medium impact acrylic resin for healthcare applications, stabilized to provide improved color after gamma sterilization. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 13 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | |||
| Ultimate | 46.2 | MPa | ASTM D638 |
| -- | 46.2 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 33 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2410 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | 34 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 32 | J/m | ASTM D256 |
| 23°C 1 | 3.1 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 81.1 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 82.8 | °C | ISO 306/B50, ASTM D1525 2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3180 µm) | 92.0 | % | ASTM D1003 |
| Haze (3180 µm) | 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 0.125 in |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4650 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Trexprene® A88BW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Elastron® G P.G401.A30.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina IVORY PVC COMPOUND -E 75800-35/ 1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OTECH PVC OW134 - Wire Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |