Hostacom EKC 265N/2 D8V689
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g1SDun_HostacomEKC265N2D8V689.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom EKC 265N/2 D8V689 is a 20% talc filled PP copolymer, with high flowability, high stiffness, high UV resistance and good scratch resistance. Product is available as a customized color matched, pellet form. This grade is delivered in D8V689 color version. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 21.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 30 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2000 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.5 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 140 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene P601-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Bamtac BTR630A | Ningbo Bamtac New Material Col, Ltd. | SBS | Bamtac |
| ARC ARC6601 | ARC Resin Corporation | Nylon 66 | ARC |
| Infino NH-1021 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| Latistat 47/7-03 | LATI S.p.A. | PP Copolymer | Latistat |