InnoTuf® HP-2170D
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g0G6Qx_InnoTuf-HP-2170D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HP-2170D is a tough, abrasion resistant elastomer formulated for hand-mix processing methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or MDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Base Resin | 1.08 | g/cm³ | |
| Cured | 1.09 | g/cm³ | |
| Hardener | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 414 | MPa | ASTM D790 |
| Flexural Strength | 18.6 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 50.0 | mg | ASTM D4060 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 750 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 20 Mix Ratio by Weight: 22 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 60 to 180 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.60 | Pa·s | |
| 25°C 2 | 3.8 | Pa·s | |
| 25°C 3 | 4.6 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 10 to 20 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 75 | ASTM D2240 | |
| Tensile Strength | 34.5 | MPa | ASTM D638 |
| Tensile Elongation at Break | 180 | % | ASTM D638 |
| Tear Strength | 140 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer P-11020-GF | Polylink Polymers (India) Ltd. | TPO | Polylink Polymer |
| RX® 3-1-501N-P | Sumitomo Bakelite North America, Inc. | DAP | RX® |
| SureSpec LD20-002 | Genesis Polymers | LDPE | SureSpec |
| KEBAFORM® C 2527 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| LEXAN™ 940 resin | SABIC Innovative Plastics | PC | LEXAN™ |