Altuglas® HFI-7 Frosted 18
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Altuglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fxIfSL_Altuglas-HFI-7-Frosted-18.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Altuglas® HFI-7 Frosted 18 is a Polymethyl Methacrylate Acrylic product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.5 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.32 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 20 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.7 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 32 | kJ/m² | ISO 179/2U |
| Notched Izod Impact Strength (23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B |
| CLTE - Flow (-30 to 23°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 1 | 1.490 | ISO 489 | |
| Transmittance | 88.0 | % | ASTM D1003 |
| Haze | 100 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 215 to 235 | °C | |
| Mold Temperature | 60.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tisoplen® PPC 10 MNF CALCITE | Tisan | PP Copolymer | Tisoplen® |
| CGPC PVC R-10X NI Bottle Blowing | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Hostacom TKS736D | LyondellBasell Industries | TPO (POE) | Hostacom |
| Sylvin 9266-70 Blue 8417 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9302-70FU Brown 7324 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |