ACCUTECH™ HP0334T30L1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fvuca1_ACCUTECH-HP0334T30L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0334T30L1 is a polypropylene homopolymer (PP Homopoly) product, which contains 30% talc filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 35.0 | MPa | ASTM D638 |
| Fracture | 30.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 | % | ASTM D638 |
| Fracture | 12 | % | ASTM D638 |
| Flexural Modulus | 3600 | MPa | ASTM D790 |
| Flexural Strength | 47.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 130 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 75.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 360E0096908 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Toyolac® AX05-X38 | Toray Resin Company | ABS | Toyolac® |
| HAIPLEN H90 C6 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| K-vinyl 105 Deg C Rating Insulation (85-Dry) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| LNP™ THERMOCOMP™ 2F004 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |