Stat-Rite® S-680
| Category: | PETG , Polyethylene Terephthalate Glycol Comonomer |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Stat-Rite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fvCnb4_Stat-Rite-S-680.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stat-Rite® S-680 is a static dissipative PETG alloy. Stat-Rite® S-680 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protection. Stat-Rite® IDP alloys provide consistent static dissipation even when thermoformed or injection molded into components. FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 28.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 350 | % | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 960 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 60.0 | °C | |
| 1.8 MPa, Unannealed | 55.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+9 | ohms·cm | ASTM D257 |
| Static Decay | |||
| 1000V to10V, 50% R.H. | 0.3 | sec | CPM |
| -5000V to -50V | 0.0100 | sec | |
| 5000V to 50V, 12% R.H. | 0.0100 | sec | FTMS 101C |
| Surface Resistance - 12% R.H. | 5.0E+8 | ohms | ESD S11.11 |
| Surface Resistivity - 50% R.H. | 2.0E+9 | ohms/sq | ASTM D257 |
| Tribocharge - Nitrile Glove | 10.0 | V | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | IDP Alloy | ||
| Ionic Content 1 | Internal Method | ||
| Cl Anion | 5.00 | ng/cm² | |
| F Anion | 2.00 | ng/cm² | |
| NO3 Anion | 3.00 | ng/cm² | |
| PO4 Anion | 2.00 | ng/cm² | |
| SO4 Anion | 5.00 | ng/cm² | |
| Non-Volatile Content 2 | 0.500 | µg/cm² | Internal Method |
| Outgassing 3 | Internal Method | ||
| MMA | 0.800 | µg/g | |
| Styrene | 0.100 | µg/g | |
| Toluene | 0.300 | µg/g | |
| Total Organics | 4.00 | µg/g |
| Note Message | |
|---|---|
| 1 . | Test Method #3010-4 |
| 2 . | Test Method #3010-5 |
| 3 . | Test Method #3010-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PVC GP K65.67 | Marco Polo International, Inc. | PVC, Rigid | MARPOL® PVC |
| Bayfit® 566 (80 Index, 3.3 pcf) | Covestro - PUR | PUR-Ether/MDI | Bayfit® |
| FRIANYL® A3 GF25 V0 | Nilit Plastics | Nylon 66 | FRIANYL® |
| Pharmalene® MP 20 PH | Versalis S.p.A. | LDPE | Pharmalene® |
| Osterlene® PPH18F | Osterman & Company | PP Homopolymer | Osterlene® |