AKROMID® B3 GF 30 S1 black 950089 (2091)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fug4Ug_AKROMID-B3-GF-30-S1-black-950089-2091-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 30 S1 black 950089 (2091) is a 30% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength Applications are housings and covers for the automotive industry and power tools |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.28 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 53.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.4 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7500 | 4200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 125 | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 6.0 | 13 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6400 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 190 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 22 | -- | kJ/m² | |
| -30°C | 25 | 22 | kJ/m² | |
| -20°C | 25 | -- | kJ/m² | |
| -10°C | 26 | -- | kJ/m² | |
| 23°C | 35 | 45 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | 120 | -- | kJ/m² | |
| -30°C | > 100 | > 100 | kJ/m² | |
| -20°C | 120 | -- | kJ/m² | |
| -10°C | 110 | -- | kJ/m² | |
| 23°C | 110 | 140 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROPRENE® 1 A80 E6N V0 | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Hostalen ACP 7740 F1 | LyondellBasell Industries | HDPE | Hostalen |
| Karina GRAY COLOR CONCENTRATE 18/485-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1301/CF/20 | LEHVOSS Group | PPS | LUVOCOM® |
| SIBUR Synthetic Rubber SBR-1705 Group I | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |