TECAMID™ 66
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger Inc. |
| Trademark: | TECAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ftscSU_TECAMID-66.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nylon was the first engineering resin. It has been used in applications ranging from electronic, marine, and automotive industries to fibers used to make carpet. Nylon has outstanding wear resistance and low frictional properties. It has very good temperature, chemical, and impact properties. However, nylon's one weakness is a propensity to absorb moisture and thus have poor dimensional stability. TECAMID® has an excellent balance of properties which make it an ideal material for metal replacement in applications such as automotive parts, industrial valves, railway tie insulators, and other industry uses whose design requirements include high strength, toughness, and weight reduction. Type 6/6 general purpose standard grade nylon. Extruded in natural and black. (Weather Resistant Black Grade is also available as a custom.) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 1.2 | % | ASTM D570 |
| Saturated, 23°C | 8.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class M, 23°C | 90 | ASTM D785 | |
| Class R, 23°C | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 25 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3030 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 107 | MPa | ASTM D790 |
| Compressive Strength | 34.5 | MPa | ASTM D695 |
| Coefficient of Friction 1(vs. Itself - Dynamic) | 0.26 | ASTM D1894 | |
| Wear Factor 2(0.28 MPa, 0.25 m/sec) | 400 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 235 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 90.0 | °C | ASTM D648 |
| Melting Temperature | 255 | °C | ASTM D2133 |
| CLTE - Flow | 8.1E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | |
| Maximum Service Temperature | |||
| Intermittent | 149 | °C | |
| Long Term | 85 | °C | UL 746B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 12 - 16 | kV/mm | ASTM D149 |
| Dielectric Constant 3 | ASTM D150 | ||
| 23°C, 60 Hz | 4.00 | ASTM D150 | |
| 23°C, 1 MHz | 3.60 | ASTM D150 | |
| Dissipation Factor (23°C, 60 Hz) | 0.010 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 |
| Additional Information |
|---|
| Data obtained from extruded shapes material. |
| Note Message | |
|---|---|
| 1 . | 40 psi, 50 fpm |
| 2 . | Against Steel |
| 3 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Delrin® AF Blend | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| Delrin® FG400MTD BLA079 | DuPont Performance Polymers | Acetal (POM) Copolymer | Delrin® |
| EPOPLEN PP CFR 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PP, Unspecified | EPOPLEN |
| LEXAN™ XHT5141 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Plenco 07487 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |