SABIC® LLDPE 726N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ftlhVA_SABIC-LLDPE-726N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 726N is a butene linear low density polyethylene resin. This grade is typically designed to give blown films a relatively high stiffness for good machinability and a good overall balance of other performance properties, such as puncture resistance, impact strength and heat sealability. Application Typical applications for SABIC® LLDPE 726N are shipping sacks, produce bags, can liners and carrier bags. SABIC® LLDPE 726N has good optical properties when blended with a LDPE (15-85%). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 220 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 240 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 13.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 14.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 45.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 35.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 650 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 850 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 160 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance - Blown Film (50.0 µm) | 650 | J/m | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 20.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 130.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 110 | °C | ISO 306/A |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film of 50 µm and BUR=2 has been produced on Kiefel IBC with 130 kg/h. Die size 200 mm, die gap 2,7 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCHPGL20 | Rainmaker Polymers LLC | PP Homopolymer | Rainmaker Polypropylene |
| Shandong PP PQ02 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| Badamid® LC70 M40 | Bada AG | Nylon 6+Nylon 66/6 | Badamid® |
| Borlink™ LE8280 | Borealis AG | PE, Unspecified | Borlink™ |
| Axiall PVC 8833 | Axiall Corporation | PVC, Flexible | Axiall PVC |