LNP™ THERMOCOMP™ WC006 compound
| Category: | Polyester, TP , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | frkvMi_LNPTHERMOCOMPWC006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP WC006 is a compound based on Polyester, TP resin containing Carbon Fiber. Also known as: LNP* THERMOCOMP* Compound WC-1006 Product reorder name: WC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.0 - 2.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.23 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 20000 | MPa | ASTM D638 |
| -- | 20700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 159 | MPa | ASTM D638 |
| Yield | 158 | MPa | ISO 527-2 |
| Fracture | 159 | MPa | ASTM D638 |
| Fracture | 158 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.2 | % | ASTM D638 |
| Yield | 1.3 | % | ISO 527-2 |
| Fracture | 1.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 15200 | MPa | ASTM D790 |
| -- | 17000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 207 | MPa | ASTM D790 |
| -- | 219 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 460 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.40 | J | ASTM D3763 |
| -- | 2.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 223 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 211 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 209 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 238 - 266 | °C | |
| Mold Temperature | 82.2 - 98.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PE SHA7260 | Braskem | HDPE | Braskem PE |
| Carbo-Rite™ B-263 | Lubrizol Advanced Materials, Inc. | PP, Unspecified | Carbo-Rite™ |
| ATTANE™ 4404G | The Dow Chemical Company | ULDPE | ATTANE™ |
| Daicel PP PT6E1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Plexar® PX6008X01 | LyondellBasell Industries | PP, Unspecified | Plexar® |