Altuglas® MI-4T
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Altuglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fpCGOF_Altuglas-MI-4T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Altuglas® MI-4T is a Polymethyl Methacrylate Acrylic product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.32 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 59.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 20 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 92.0 | MPa | ISO 178 |
| Compressive Stress (23°C) | 91.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/2U |
| Notched Izod Impact Strength (23°C) | 2.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 102 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 98.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 106 | °C | ISO 306/B |
| CLTE - Flow (-30 to 23°C) | 7.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 2090 | J/kg/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.040 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 1 | 1.490 | ISO 489 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 230 to 240 | °C | |
| Mold Temperature | 75.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BR3XBK6550 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Ultramid® C33 01 | BASF Corporation | Nylon 66/6 | Ultramid® |
| INEOS EBA B30G730 | INEOS Olefins & Polymers Europe | EBA | INEOS EBA |
| Vipel® F774-APT-20 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| SQUARE® LSG1001-09A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |