Durethan® C 38 F 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | foppSp_Durethan-C-38-F-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6-Copolymer, non-reinforced, extrusion, medium viscosity, no additives, high transparency |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.13 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 5.00 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 10 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 212 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | -- | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | -- | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C, 1 MHz) | -- | 3.00 | IEC 60250 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6/IPDI, ET, 18-020 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCA-4515X | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Multiuse Leostomer® LJ-3140N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| Evermore PUR SA-2018MP | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Luranyl® KR 2454/3 G2 | ROMIRA GmbH | PPE+PS | Luranyl® |
| Badaflex® TPU 90A 8030 CF17 | Bada AG | TPU, Unspecified | Badaflex® |