LNP™ LUBRICOMP™ DX98306H compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fol1rw_LNP-LUBRICOMP-DX98306H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible. Also known as: LNP* LUBRICOMP* Compound PDX-D-98306 LE EES Product reorder name: DX98306H |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.48 | g/cm³ | ASTM D792 |
| -- | 1.29 | g/cm³ | ISO 1183, ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.10 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Flow : 3.20 mm | 0.30 to 0.50 | % | Internal Method |
| Across Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.74 | % | ISO 294-4 |
| Flow : 24 hr | 0.64 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Saturation, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5090 | MPa | ASTM D638 |
| -- 2 | 2070 | MPa | ASTM D638 |
| -- | 2140 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 51.0 | MPa | ASTM D638, ISO 527-2 |
| Break | 42.7 | MPa | ASTM D638 |
| Break 3 | 43.0 | MPa | ASTM D638 |
| Break | 43.0 | MPa | ISO 527-2 |
| Break | 48.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield | 5.3 | % | ASTM D638, ISO 527-2 |
| Break | 33 | % | ASTM D638 |
| Break 4 | 2.3 | % | ASTM D638 |
| Break | 38 | % | ISO 527-2 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 5010 | MPa | ASTM D790 |
| -- | 2070 | MPa | ASTM D790 |
| -- | 2100 | MPa | ISO 178 |
| -- 6 | 5130 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 71.0 | MPa | ISO 178 |
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 7 | 85.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.37 | ||
| vs. Itself - Static | 0.32 | ||
| Wear Factor - Washer | 21.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8(23°C) | 5.8 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 69 | J/m | ASTM D256 |
| 23°C | 150 | J/m | ASTM D256 |
| -30°C 9 | 5.5 | kJ/m² | ISO 180/1A |
| 23°C 10 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1800 | J/m | ASTM D4812 |
| 23°C 11 | 180 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 34.1 | J | ASTM D3763 |
| -- | 32.9 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 132 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 133 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 123 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ASTM D1525, ISO 306/B50 11 14 |
| -- | 145 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.700 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| 14 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ CP0437C10L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Globalene® ST611M | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| Enviramid® N1320MG8HL BK | Ravago Manufacturing Americas, LLC | Nylon 66 | Enviramid® |
| Hanwha Total PP RP100G160 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| PENTAMID B GV40 E H schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |