CERTENE™ LLHF-122D
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | foYN20_CERTENE-LLHF-122D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLHF-122D is a certified prime resin containing Hexene-comonomer designed for production of superior strength and low stiffness Blown films. LLHF-122D features easy processability and films exhibit high impact strength, very good tear and excellent creep resistances. LLHF-122D major applications include heavy duty bags, high strength liners, grocery bags and frozen food packaging. Maxim um recommended film drawdown is 0.5 mil. LLHF-122D contains medium slip and high antiblock. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 230 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 260 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 12.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 57.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 41.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 630 | % | ASTM D882 |
| TD : Break, 25 µm | 880 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 350 | g | ASTM D1922 |
| TD : 25 µm | 8000 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 60 | ASTM D2457 | |
| Haze (25.4 µm) | 9.5 | % | ASTM D1003 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 215 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BR15NT6504 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Galloo GP-PP-1065 | Galloo Plastics | PP, Unspecified | Galloo |
| Iupiace® EHM1010A | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| KEBAFLEX® SG 60 A.01 | BARLOG plastics GmbH | TES | KEBAFLEX® |
| ESTOPLAST XU 64151NN01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |