Tarnamid® T- 27 CF10
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fnRg0Q_Tarnamid-T--27-CF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| It is 10% carbon fibre reinforced polyamide 6 compound, heat stabilised, good conductive and electrostatic properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 60.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.90 | % | |
| Flow : 2.00 mm | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 200 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6700 | MPa | ISO 178 |
| Flexural Stress 2 | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 42 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Limit of Temperature - a few hours operation | < 200 | °C | |
| Temperature Index | |||
| 20000 hr | 110 | °C | |
| 5000 hr | 120 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | + | FMVSS 302 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | PA6, MHRZ, 14-080, CF10 | ISO 1874 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+8 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP513-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Styropor® F 315 E | BASF Corporation | PS (EPS) | Styropor® |
| Titalon® 1252ES | Titan Plastics Compounds Co., Ltd. | Nylon 6 | Titalon® |
| UNITIKA Nylon 6 EX-1222 | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| THERMOLAST® V TV8VAZ (Series: LTP/PA) | KRAIBURG TPE | TPE | THERMOLAST® V |