EMERGE™ PC/ABS 7700 EU Advanced Resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. It has superior processability for injection molding applications. This grade has excellent aesthetics, is UV stabilized and is available in custom colors. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| shrinkage- Flow | 0.40 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20, injection molding | 2550 | MPa | ASTM D638 |
| 4.00, injection molding | 2500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield, 3.20mm, injection molding | 57.0 | MPa | ASTM D638 |
| Yield, 4.00mm, injection molding | 56.0 | MPa | ISO 527-2/50 |
| Fracture, 3.20mm, injection molding | 48.0 | MPa | ASTM D638 |
| Fracture, 4.00mm, injection molding | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield, 3.20mm, injection molding | 3.8 | % | ASTM D638 |
| Yield, 4.00mm, injection molding | 3.8 | % | ISO 527-2/50 |
| Fracture, 3.20mm, injection molding | 100 | % | ASTM D638 |
| Fracture, 4.00mm, injection molding | 52 | % | ISO 527-2/50 |
| Flexural Modulus (23°C, 4.00 mm, Injection Molded) | 2450 | MPa | ASTM D790 |
| Flexural Strength (23°C, 4.00 mm, Injection Molded) | 86.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, injection molding | 16 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 50 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/A | ||
| -30°C, injection molding | 17 | kJ/m² | ISO 180/A |
| 23°C, injection molding | 50 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 89.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 78.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ISO 306/A120 |
| -- | 94.0 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.2E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 1.60mm, in oil | 26 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 2.86 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 7.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm 1 | V-0 | UL 94 | |
| 2.0 mm 2 | 5VB | UL 94 | |
| 2.5 mm 3 | 5VA | UL 94 | |
| Glow Wire Flammability Index 4(2.0 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 240 - 275 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Note Message | |
|---|---|
| 1 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 2 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SITRALON 18E-TF10-HK / C7043 Dark Grey | SITRAPLAS GmbH | PC | SITRALON |
| Sylvin 8741-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| APEX® 3070-H | Teknor Apex Company | PVC, Flexible | APEX® |
| DOMAMID® 6G10 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| EcoLon® 2200-BK1 | Wellman Engineering Resins | Nylon 66 | EcoLon® |