Order Products : sales@su-jiao.com
Later 4
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Later |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fnKtvI_Later-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polybutylene Terephtalate (PBT). |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.7 to 2.0 | % | |
| Flow : 2.00 mm | 1.7 to 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2100 | MPa | |
| 60°C | 650 | MPa | |
| 90°C | 400 | MPa | |
| 120°C | 350 | MPa | |
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 40 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 190 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 195 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.1E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 245 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ MN-818.S001-8000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| SABIC® HDPE CC3054 | Saudi Basic Industries Corporation (SABIC) | HDPE Copolymer | SABIC® HDPE |
| HAIPLEN H10 T8 HT | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Panlite® LV-2250Z | TEIJIN LIMITED | PC | Panlite® |
| Lusin® Clean 1020 | Chem-Trend L.P. | TP, Unspecified | Lusin® |