XANTAR® XRM 5010
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fmzI5Z_XANTAR-XRM-5010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC-GF9 FR(76) 9% Glass Reinforced. Flame Retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.55 | % | |
| Flow | 0.20 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.31 | % | ISO 62 |
| Limiting Viscosity Number | 45.0 | cm³/g | ISO 1628-4 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity of Melt | 0.26 | W/m/K |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 15 | % | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | ||
| -- 1 | 30.0 | J | |
| -- 2 | 40.0 | J | |
| Film Puncture Force | ISO 6603-2 | ||
| -- 3 | 4400 | N | |
| -- 4 | 4200 | N |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (3.00 mm) | V-0 | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 35 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | -30°C |
| 2 . | 23°C |
| 3 . | -30°C |
| 4 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNPRENE® FF40FB | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| Kumho PS HFH 407 | Korea Kumho Petrochemical Co., Ltd. | PS (IRPS) | Kumho PS |
| LNP™ THERMOCOMP™ RF006XXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Sylvin 3250-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Axiall PVC 19751 | Axiall Corporation | PVC, Flexible | Axiall PVC |