Mirel™ P4001
| Category: | PHA , Polyhydroxyalkanoate |
| Manufacturer: | Metabolix |
| Trademark: | Mirel™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | flYthE_Mirel-P4001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Mirel™ P4001 is a general purpose, high melt strength material suitable for cast sheet extrusion. Mirel™ P4001 is designed for a wide range of sheet applications including gift cards, promotional materials, indoor/outdoor signage, plant pots and plant tags. Mirel™ P4001 can be processed on conventional extrusion equipment with either an up-stack or down-stack roll configuration. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 1900 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648B | ||
| 0.45 MPa, not annealed | 110 | °C | ASTM D648B |
| 1.8 MPa, not annealed | 57.0 | °C | ASTM D648B |
| Vicat Softening Temperature | 133 | °C | ASTM D1525 1 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (180°C, 100 sec^-1) | 1200 | Pa·s | ASTM D3835 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Cylinder Zone 1 Temp. | 175 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 165 | °C | |
| Melt Temperature | 165 - 170 | °C | |
| Die Temperature | 165 | °C | |
| Extruder Screw Compression Ratio 2 |
| Extrusion instructions |
|---|
| A-roll (Top roll of a down-stack): <32°CB-roll (Middle roll): 50 to 65°CC-roll (Bottom roll of a down-stack): 65°C |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 压 力1 (10N) |
| 2 . | Any mixing sections should be low shear design. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecodur® PB70 GR50 BK002 CA01 | Eurotec Engineering Plastics | PBT+PET | Tecodur® |
| Sinpolene HFR8018 | Teknor Apex Asia Pacific PTE. LTD. | TP, Unspecified | Sinpolene |
| Nycal™ 1820H Bk-1 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| Akulon® S223-HG7 | DSM Engineering Plastics | Nylon 66 | Akulon® |
| Telcar® TL-1431H | Teknor Apex Company | TPE | Telcar® |