NORYL GTX™ GTX830 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fkdIFe_NORYLGTXGTX830resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GR 30%. Highest stiffness of 1200000 psi (8200 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: under the bonnet. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.20 - 0.30 | % | Internal method |
| Transverse flow : 3.20mm | 0.65 - 0.85 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr, 50% RH | 0.50 | % | ASTM D570 |
| Balance, 50% RH | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 152 | MPa | ASTM D638 |
| Fracture | 159 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 8580 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 100 mm Span) | 248 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 80 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 254 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 241 | °C | ASTM D648 |
| Vicat Softening Temperature | 249 | °C | ASTM D1525 5 |
| CLTE - Flow (-20 to 150°C) | 2.0E-5 - 3.1E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 6 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 2 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 266 - 304 | °C | |
| Middle Temperature | 271 - 304 | °C | |
| Front Temperature | 277 - 304 | °C | |
| Nozzle Temperature | 282 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 76.7 - 121 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 标准 B (120°C/h), 载荷2 (50N) |
| 6 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8233G HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| Axiall PVC 59996J | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Jackdaw PC DX10GY6590 | Jackdaw Polymers | PC | Jackdaw PC |
| Karina CLEAR PVC COMPOUND -E 84/203-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina GREEN PVC COMPOUND 700D40/356-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |