DOMAMID® A1-004-V40-N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics GmbH |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fho0mb_DOMAMID-A1-004-V40-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, medium viscosity, 40% glass fiber reinforced, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Water Absorption 1 | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 145 | cm³/g | ISO 307 |
| Ash Content (650°C) | 40 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 217 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 200 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 2 | 10000 | MPa | ISO 178 |
| Flexural Stress 3 | 310 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 110 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 217 | °C | ISO 306/A50 |
| -- | 214 | °C | ISO 306/B50 |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | VDE 0303-3 |
| Volume Resistivity | 1.0E+15 | ohms·cm | VDE 0303-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(2.00 mm) | 23 | mm/min | ISO 3795 |
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Ignition Temperature | VDE 0471/2 | ||
| 2.00 mm | 700 | °C | |
| 3.00 mm | 700 | °C |
| Note Message | |
|---|---|
| 1 . | 24 hrs |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Keliren® CM352F | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| Polyrocks EP8400XD105FVH-1 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |
| Sylvin 9710-80FUV Blue 8335 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8972-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CERTENE™ 740 | Muehlstein | ABS | CERTENE™ |