Lionpol LC-62306
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Lion Polymers Incorporated |
| Trademark: | Lionpol |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fhkW4y_Lionpol-LC-62306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lionpol LC-62306 is a thermoplastic elastomer (TPE) product,. It is available in North America. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.1 - 3.5 | % | ASTM D955 |
| Transverse flow | 2.1 - 3.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 6 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 0.0965 | MPa | ASTM D412 |
| Tensile Strength (Break) | 3.10 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1200 | % | ASTM D412 |
| Compression Set | ASTM D395 | ||
| 70°C, 22 hr | 19 | % | ASTM D395 |
| 100°C, 22 hr | 41 | % | ASTM D395 |
| Additional Information |
|---|
| Permanent Set: 2% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 141 - 179 | °C | |
| Front Temperature | 163 - 202 | °C | |
| Nozzle Temperature | 163 - 202 | °C | |
| Mold Temperature | 21.1 - 32.2 | °C | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6911 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RELENE® 52GB001 | Reliance Industries Limited | HDPE, HMW | RELENE® |
| Sylvin 9067F3 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| YUCLAIR® FG400 | SK Global Chemical | LLDPE | YUCLAIR® |
| LUVOCOM® 1105-1963 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |