Jampilen HP648S

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	Jam Polypropylene Company
Trademark:	Jampilen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fhDrTy_Jampilen-HP648S.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Jampilen HP648S is a high melt flow homopolymer with a narrow molecular weight distribution. Jampilen HP648S is designed for the high speed injection molding of thin-walled items with a good transparency and optimum antistatic properties. Due to its outstanding flow properties, its very high stiffness and excellent dimensional stability, this grade can be molded at very high speeds producing thin-walled parts, even with complicated shapes, without distortion. In many of applications Jampilen HP648S can replace traditional materials such as polystyrene since the product exhibits excellent processability, low residual stress, low shrinkage and warpage on top of the advantages typical of polypropylene such as light weight, low odour transfer, high chemical resistance and a good balance of mechanical properties.

General Information
Additive	Antistatic
Features	Antistatic Fast Molding Cycle Good Chemical Resistance Good Dimensional Stability High Clarity High Flow High Strength Homopolymer Low Odor Transfer Low Residuals Low Shrinkage Low Warpage Narrow Molecular Weight Distribution
Uses	Business Equipment Caps Closures Consumer Applications Cosmetic Packaging Food Packaging Media Packaging Thin-walled Packaging White Goods & Small Appliances Writing Instruments
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	35	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	102		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	35.0	MPa	ASTM D638
Tensile Elongation (Yield)	10	%	ASTM D638
Flexural Modulus	1500	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	29	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	110	°C	ASTM D648
Vicat Softening Temperature	155	°C	ASTM D1525 ¹
Accelerated Oven Ageing (150°C)	360	hr	ASTM D3012

Note Message
1 .	Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Mold Max® 25	Smooth-On, Inc	Silicone	Mold Max®
CERTENE™ LLHF-123F	Muehlstein	LLDPE	CERTENE™
DINALON® A1X25 G30V0	Grupo Repol	Nylon 66	DINALON®
Laril 13 G/30	LATI S.p.A.	PPE+PS	Laril
Sylvin 9915-55 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin