LNP™ THERMOCOMP™ 2F005 compound
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fhCORh_LNP-THERMOCOMP-2F005-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 2F005 is a fluoropolymer compound based on ETFE containing 25% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound FP-EF-1005 Product reorder name: 2F005 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.87 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.010 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6190 | MPa | ASTM D638 |
| -- | 5680 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 61.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/5 |
| Break 3 | 59.0 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 6.6 | % | ISO 527-2/5 |
| Break 5 | 8.2 | % | ASTM D638 |
| Break | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 5480 | MPa | ASTM D790 |
| -- 7 | 5200 | MPa | ISO 178 |
| Flexural Stress | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 530 | J/m | ASTM D256 |
| 23°C 8 | 45 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 9 | 91 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 21.6 | J | ASTM D3763 |
| -- | 10.7 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 248 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 232 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 190 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 132 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 300 to 325 | °C | |
| Front Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | 315 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GP1001MD | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Xuchuan XCW-6355B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Complet® LGF30-TPU | PlastiComp, Inc. | ETPU | Complet® |
| Karina LIGHT BEIGE MBU -E 08/494-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kangxi® FRPP-V0 | Wuxi Kangxi Plastics Technology Co.,Ltd. | PP, Unspecified | Kangxi® |