ESTAPROP H 05100GFC
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Cossa Polimeri S.r.l. |
| Trademark: | ESTAPROP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ffkVvg_ESTAPROP-H-05100GFC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ESTAPROP H 05100GFC is a Polypropylene Homopolymer (PP Homopolymer) product filled with 50% glass fiber. It is available in Europe. Typical application: Furniture. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12500 | MPa | ASTM D638 |
| Tensile Strength (Break) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strain at Break | 150 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 110 | J/m | |
| 0°C | 130 | J/m | |
| 23°C | 150 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 155 | °C | ASTM D648 |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP340N | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Moplen EP380S | PolyMirae | PP Copolymer | Moplen |
| Elastane™ 4721R10 | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Karina WHITE PVC 837-10/ 55-AY-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ HF1130 resin | SABIC Innovative Plastics | PC | LEXAN™ |